Liquid Fire Retardant Epoxy , Carboxylic Anhydride Chemical Resistance Epoxy Hardener
  • Liquid Fire Retardant Epoxy , Carboxylic Anhydride Chemical Resistance Epoxy Hardener
  • Liquid Fire Retardant Epoxy , Carboxylic Anhydride Chemical Resistance Epoxy Hardener
  • Liquid Fire Retardant Epoxy , Carboxylic Anhydride Chemical Resistance Epoxy Hardener

Liquid Fire Retardant Epoxy , Carboxylic Anhydride Chemical Resistance Epoxy Hardener

Place of Origin HUBEI, CHINA
Brand Name JT
Certification ISO
Model Number JT-RESIN 002
Product Details
TG:
90-100
MIXING RATION:
100/100/380
COLOR:
COLOR PASTE / RED
VOLTAGE TYPE:
LOW
Sample Curing Conditions:
10h @140℃
Properties:
Flame Retardancy
Compound:
3
High Light: 

Liquid Fire Retardant Epoxy

,

Chemical Resistance Epoxy Hardener

,

Carboxylic Anhydride Chemical Resistance Epoxy

Payment & Shipping Terms
Minimum Order Quantity
20kg
Price
negotiable
Packaging Details
drum
Product Description

Flame Retardance Epoxy Resin Compound Carboxylic Anhydride Hardener CE

TDS:

 

JT 002A Epoxy Resin 100 pbw

JT 002B Epoxy Hardener 100 pbw

 

 

Liquid, Latent, Silica flour filled, hot-curing cast resin system. Specially formulated for convenient in processing with excellent impregnating performance.

 

 

Instrument transformers and Dry type distribution transformer.

Applications

 

Conventional casting with stage wise curing, or pressure gelation or Processing methods

Automatic pressure gelatin casting (PG or APG process).

 

 

 

Long pot-life, short gel-time under high temperature

Excellent mechanical and electrical properties

Excellent crack resistance

 

 

 

Properties

 

Hubei Jiangte Insulation Composite Guangzhou Jiangte Insulation Composite Add:No.219,Zhanghua Rd(N),Economic & Development Add:Rm606,DongHong International Plaza, No.

Zone of Qianjiang City, Hubei Province, China. 113, Chebei Rd, Tianhe District, Guangzhou,China.

Tel:+86-728-6201068 Tel:+86-20-82320316

Fax:+86-728-6202066 Fax:+86-20-82315407

 

 

 

Liquid Fire Retardant Epoxy , Carboxylic Anhydride Chemical Resistance Epoxy Hardener 0Liquid Fire Retardant Epoxy , Carboxylic Anhydride Chemical Resistance Epoxy Hardener 1

Product data (guideline values)

 

Liquid, prefilled, solvent-free epoxy resin  
JT 8058A Aspect   Visual - Red paste
Viscosity At 40℃ ISO2555:1989 Mpa.s 2000 - 5000
(test with Brookfield viscometer)  
Specific weight At 20℃ ISO2811-2:1997 g/cm3 1.55 - 1.62
Filler content % by weight 47 - 52
Liquid, modified, prefilled and pre-accelerated anhydride hardener  
JT 8058B Aspect   Visual - Red paste
Viscosity At 40℃ ISO2555:1989 Mpa.s 1500 - 3000
(with Brookfield viscometer)  
Density At 20℃ ISO2811-2:1997 g/cm3 1.70 - 1.80
Filler content b % by weight 52 - 58

JT 8055B contains accelerator. Prolonged storage at high ambient temperatures results in an undesirable increase in its viscosity and impairs the reactivity of the system mix.

It is sensitive to moisture. Partly emptied containers must be resealed immediately.

 

 

 

Remark Prefilled liquid products always show small filler sedimentation.

Before partial use we recommend to stir up carefully the components or to use each

container as complete unity

 

 

Storage The components have to be stored under dry conditions at 5 - 25°C in tightly sealed

original containers. Under these conditions, the shelf life will correspond to the expiry

date stated on the label. After this date, the product may be processed only following

re-analysis. Partly emptied containers should be closed tightly immediately after use.

For information on waste disposal and hazardous products of decomposition in the

event of fire, refer to the Material Safety Data Sheets (MSDS) for these particular products.

 

             

 

Mechanical and Physical Properties (guideline value)
Tested system:        
JT 8600A / JT 8600B
Mixing Ratio:100/80 pbw    
Determined on standard test specimen at 23°C
cured for 6 hours at 80°C then 4 hours at 100C and then 6hours at 130°C
 

Tensile strength ISO R 527: 1993 N/mm² 65 - 78

Elongation at break % 1.8 - 2.0

E modulus from tensile test N/mm² 8000 - 9500

 

Flexural strength ISO 178: 2001 MPa 110 - 125

Surface strain % 1.5 - 1.7

E modulus MPa 8000 - 9500

 

Critical stress intensity factor (K IC ) MPa·m ½ 2.4 - 2.6

 

Glass transition temperature ISO 11357-2: 1999°C 65 - 80

 

Coefficient of linear thermal expansion ISO 11359: 1999

Mean value below Tg ppm/K 40 - 43

 

Water absorption (specimen: 50x50x4 cm) ISO 62

60 min at 100°C % by wt. 0.15 - 0.20

 

Density at 20°C g/cm³ 1.65 – 1.75

Thermal life Class (20000h)

 

                                                                                                                                                                                    

PRODUCT NAME:

Epoxy Electrical Insulation System

Liquid Fire Retardant Epoxy , Carboxylic Anhydride Chemical Resistance Epoxy Hardener 2

                                                                                                                                                                                                 

 

 

Liquid Fire Retardant Epoxy , Carboxylic Anhydride Chemical Resistance Epoxy Hardener 3

Liquid Fire Retardant Epoxy , Carboxylic Anhydride Chemical Resistance Epoxy Hardener 4

 

Client Product:

Liquid Fire Retardant Epoxy , Carboxylic Anhydride Chemical Resistance Epoxy Hardener 5

Equipment used by customers:

Liquid Fire Retardant Epoxy , Carboxylic Anhydride Chemical Resistance Epoxy Hardener 6Liquid Fire Retardant Epoxy , Carboxylic Anhydride Chemical Resistance Epoxy Hardener 7

 

Hubei Plant and Guangdong Plant:

Liquid Fire Retardant Epoxy , Carboxylic Anhydride Chemical Resistance Epoxy Hardener 8

Liquid Fire Retardant Epoxy , Carboxylic Anhydride Chemical Resistance Epoxy Hardener 9

 

ISO certifcate:

Liquid Fire Retardant Epoxy , Carboxylic Anhydride Chemical Resistance Epoxy Hardener 10

 

Part of our customers:

Liquid Fire Retardant Epoxy , Carboxylic Anhydride Chemical Resistance Epoxy Hardener 11

Liquid Fire Retardant Epoxy , Carboxylic Anhydride Chemical Resistance Epoxy Hardener 12

 

 

FAQ:

 

1. What’s the Pre-filled?

Pre-filled is the resin or hardener has been filled with silica sands before delivering to you.

 

2. Is Pre-filled resin cheaper than Pure resin?

Generally it is. However, you should consider the final cost. If you can find qualified silica sands in you local market, the pure resin is better choice. Silica sands are very cheap, sea freight cost is high. With same quantity of resin in a shipment, you can get more final mixed resin with local silica sands.

 

3. Why JiangTe resin doesn’t offer Flexibilizer and Accelerator?

We’ve added them into resin/hardener already before delivering to you. So you can use our materials easily

Contact Us at Any Time

86-20-82320316
Room 606, Donghong International Plaza, No. 113 Chebei Road, Tianhe District, Guangzhou, China
Send your inquiry directly to us